The RINA FH32 shipbuilding steel plates have yield strength of 45,500 psi (315 MPa), and ultimate tensile strength of 64,000 - 85,000 psi (440-590 MPa). All the RINA FH32 shipbuilding steel plate offered by Katalor Industry can be certificated by Registro Italiano Navale (RINA).
RINA FH32 Shipbuilding steel plates can be used for producing container and bulk cargo vessels as well as cruise ships, ferries and yachts.
| Grade |
C % |
Si % |
Mn % |
P % |
S % |
V % |
AL % |
Cr % |
|
RINA Grade FH32 |
0.160 |
0.1-0.5 |
0.90-1.6 |
0.025 |
0.025 |
0.05-0.10 |
0.015 |
0.200 |
|
Cu % |
Mo % |
Nb % |
Ni % |
Ti % |
N % |
|
|
|
|
0.350 |
0.080 |
0.02-0.05 |
0.800 |
0.020 |
0.009 |
|
|
| Grade |
Thickness(mm) |
MinYield(Mpa) |
Tensile(Mpa) |
Elongation (%) |
Min Impact Energy |
|
|
RINA Grade FH32 |
8mm-50mm |
Min 315Mpa |
440-590Mpa |
22% |
-60 |
34J |
|
51mm-70mm |
Min 315Mpa |
440-590Mpa |
22% |
-60 |
41J |
|
|
71mm-100mm |
Min 315Mpa |
440-590Mpa |
22% |
-60 |
50J |
|
|
The min impact energy is longitudinal energy |
||||||
| Thickness |
3-150mm |
|
Width |
1220-4200mm |
|
Length |
5000-18000mm |
Notes: coil thickness ≤ 25mm
RINA FH32 Shipbuilding steel plates are mainly used for making the hull of ship building and ship repairing, the offshore oil drilling platform, the platform pipe joints and other components. RINA FH32 shipbuilding steel plate is a kind of hot rolled high tensile strength steel. RINA FH32 shipbuilding steel plate can achieve the impact toughness at Celsius degree -60°. welcome to contact katalor if you are looking for RINA FH32 shipbuilding steel plate supplier.