13CrMoV9-10 steel machining parts owned a higher tensile strength within 580-780Mpa. 13CrMoV9-10 steel structures are mainly used for manufacturing boilers, pressure vessels. Katalor Enterprises are mainly engaged in steel structure, such as cutting, drilling, milling, turning, bending, welding etc. We have the ability to produce many kinds of steel machining parts. We can also offer the heat treatment service, such as annealing, normalizing, hardening, tempering, hardening and tempering, solution treatment etc.
|
Steel Grade |
Chemical Composition % |
|||||||||||||||
|
Steel name |
Steel number |
C |
Si |
Mn |
P |
S |
Al |
N |
Cr |
Cu |
Mo |
Nb |
Ni |
Ti |
V |
other |
|
13CrMoV9-10 |
1.7703 |
0.11-0.15 |
≤0.10 |
0.30-0.60 |
0.015 |
0.005 |
|
≤0.012 |
2.00-2.50 |
≤0.20 |
0.90-1.10 |
≤0.07 |
≤0.20 |
0.03 |
0.25-0.35 |
≤0.002B |
|
Steel Grade |
General delivery conditions |
steel thickness |
Room temperature tensile |
impact energy KV，J |
|||||
|
yield strength |
Tensile strength |
Elongation |
|||||||
|
Steel name |
Steel number |
mm |
MPa |
MPa |
% |
- 20 |
0 |
+ 20 |
|
|
13CrMoV9-10 |
1.7703 |
+ NT |
≤ 60 |
455 |
600～ 780 |
18 |
27 |
34 |
40 |
|
60 < t≤ 150 |
435 |
590～ 770 |
|||||||
|
+ QT |
150 < t≤ 250 |
415 |
580～ 760 |
||||||
High tension test, Low temperature impacting test, Simulated post-welded heat treatment (PWHT).
13CrMoV9-10 steel machining parts Range (T*W*L): according to customer’s drawings.
13CrMoV9-10 steel work Testing equipment: Universal testing machine, Torque Tester, Axial force tester, torque tester, Coating thickness gauge etc.
As the professional Chinese 13CrMoV9-10 steel machining parts supplier, we will supply our customers the best quality with the competitive price, the best service and rapid delivery time. If you want to purchase the 13CrMoV9-10 steel structure, we will support you to pay a visit to our company and do inspection. If you have any need of 13CrMoV9-10 steel, please be free to contact me. We are sincerely looking forward to cooperate with you.