Raex500 Steel Plates

Raex500 steel is a bendable and weldable abrasion-resistant steel, with a nominal hardness of 500 HBW. This material is suitable for applications that demand higher wear resistance. Raex500 steel sheet is available in thicknesses of 3 to 6.5 mm and Raex500 steel plate in thicknesses of 6 to 80 mm. Maximum width is depending on thickness. More detailed information on dimension, sizes and shapes, please contact us.

Raex500 Steel Plates Chemical Composition(%)

Material	C max .	Si max .	Mn max .	P max .	S max .	Cr max .	Ni  max .	Mo max .	B max .
RAEX 500	0.30	0.80	1.70	0.025	0.015	1.50	1.00	0.50	0.005

Raex500 Steel Plates Mechanical Properties:

Material	Hardness (HBW)	Typical yield strength (MPa)	Tensile strength(MPa) min.	Elongation % min.
RAEX 500	470 - 540	1300	1600	8

Note: Brinell Hardness is measured, according to EN ISO 6506-1 on milled surface 0.3-3.0mm below surface. Hardness value is being announced in the material certificate. Mechanical properties are tested in transverse direction and tabulated for information only and values are not shown in material certificate.

Raex500 Steel Plate Thickness

For plate tolerances according to EN 10 029 Class A, tighter tolerances upon agreement. For sheet tolerances according to EN 10 051 Category A.
Length and Width
For plate tolerances according to EN 10 029, tighter tolerances upon agreement. For sheet tolerances according to EN 10 051.
Shape
For plate tolerances according to EN 10 029. For sheet tolerances according to EN 10 051.
Flatness
For plate and sheet the flatness deviation is max 6 mm/m.
Surface Properties
According to EN 10 163-2 Class A, Subclass 3.
 