C50 / C50E is medium carbon steel with high strength steel. It is usually used in normalizing, quenching or tempering condition. C50 / C50E steel is used in the manufacture of mechanical products and spring pieces, such as forging gear, tie rod, roller, shaft, friction plate, agricultural spindle dig plowshares and heavy-duty spindle bearing,etc. C50 / C50E steel are also with high wear resistance property.
C: 0.47-0.55, Si: 0.4, Mn: 0.6-0.9, P: 0.03, S: 0.035, Cr: 0.4, Mo: 0.1, Ni: 0.4
C50/ C50E: diameter≤16mm or thickness≤8mm
Tensile strength σb (MPa):750-900
Yield strength σs (MPa):≥520
Elongation δ5 (%):≥13
C50/ C50E: 16mm < diameter≤40mm or 8mm < thickness≤20mm:
Tensile strength σb (MPa):700-850
Yield strength σs (MPa):≥460
Elongation δ5 (%):≥15
C50/ C50E: 40mm < diameter≤100mm or 20mm < thickness≤60mm:
Tensile strength σb (MPa):650-800
Yield strength σs (MPa):≥400
Elongation δ5 (%):≥16
Recommended temperature in heat treatment: Normalizing: 830℃,Quenching:830℃, tempering 600℃
SAE J403 1050 steel, JIS G4051 S50C steel
heat treatment (Q+T, annealing, normalizing or high temperature tempering) , without heat treatment.
Based on positive and pragmatic attitude, efficient management system, and perfect after-sale service, Shanghai Katalor guarantees to provide you with the best C50, C50E steel plates, round bar or steel tube/pipe. With our strong machining service, we can process the C50 and C50E raw material into C50/C50E steel works, steel structures and steel machining parts. If you have any needs, please feel free to contact us. We can offer you the technical support according to your demand, and also will offer you best quality and service.