N155/ N-155 High temperature strength nickel alloy steel material

Date : 2016-04-21 13:15:57

Nickel-based N155 alloy has a long history, back to 1950, of high strength at temperatures up to 1500 F and is capable of sustaining moderate loading at temperatures of 2000 F. It has good oxidation resistance at high temperature and also possesses good corrosion resistance to sulfuric acid (at room temperature) and to nitric acid. High temperature strength derives directly from the chemical composition of the alloy and is not dependent upon age hardening.

Application: Oxidation resistance nickel alloy N-155 used in Industrial furnace structural parts and fixtures. High temperature bolts and gas turbine combustion chambers, exhaust manifolds, and turbine blades. N-155 alloy is used in numerous aircraft applications such as tail cones and tailpipes, exhaust manifolds, combustion chambers, afterburners, turbine blades and buckets, and bolts.

Forming by cold working is preferred and the high strength N155 nickel alloy has good ductility. It does work harden and may require a solution heat treatment to restore ductility during cold forming.

Typical Mechanical Properties for N-155 nickel alloy (Tensile Properties)


Test
Temperature

Tensile
Strength

Yield Strength
0.2% Offset

%
Elongation
in 2"

%
Reduction
of Area

°F

°C

ksi

MPa

ksi

MPa

Room
1000
1200
1400
1600
1800
2000

Room
538
649
760
871
982
1093

118
93
80
60
38
19
10

314
641
552
414
262
131
69

59
44
42
38
26
18
--

407
303
290
262
179
124
--

40
37
35
35
37
38
45

50
48
47
42
42
50
60

Typical Mechanical Properties for N155 nickel alloy(Stress Rupture Properties)


Test
Temperature

Stress for Rupture in

°F

°C

10 Hours

100 Hours

1000 Hours

ksi

MPa

ksi

MPa

ksi

MPa

1200
1350
1500
1650

649
732
816
899

65
38
26
18

448
262
179
124

52
30
18
10

359
207
124
69

38
23
14
7

262
159
97
48

Chemical composition for N-155 nickel alloy 


Element

Min

Max

Carbon

0.08

0.16

Manganese

1.00

2.00

Silicon

--

1.00

Sulfur

--

0.03

Chromium

20.0

22.5

Nickel

19.0

21.0

Copper

--

0.50

Tungsten

2.00

3.00

Iron

Balance

Cobalt

18.5

21.0

Columbium*

0.75

1.25

Nitrogen

0.10

0.20

Molybdenum

2.50

3.50

Phosphorus

--

0.04

Nickel-based N155 / N-155 alloy Specifications:
Round bar steel:dia 1mm to 2000mm
Square-shape steel: 50mm  to  600mm
Plate steel thickness:0.1mm  to  800mm
Width: 10mm to 1500mm
Length: We can supply any length based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubing: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/ quenching + tempering
Surface conditions: scaled (hot working finish)/ground/rough machining/ fine machining
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any imperfections

ShangHai Katalor have a high quality logistics team who make sure the fast delivery time and shipment. Anyway, if you want to find high strength N155 nickel alloy please contact us. We will give you the N155 competitive price, N-155 alloy good quality and best service from us.

Contact Us

TEL : 0086-18317160019

E-mail : [email protected] 

Address : No.230,1st Floor,Building No.1,No.221 Of Huashen Road,Free Trade Area Of Pudong New District,Shanghai China