58crv4 steel structure is widely used in quenched and subsequently tempered steel for extremely wear resisting components, driving components, gears. for more information about 58crv4 steel structure , please see the following :
58crv4 steel structure chemical composition (WEIGHT %)
C(%): 0.55~0.62
Si(%): 0.15~0.40
Mn(%): 0.70~1.10
P(%)≤: 0.035
S(%)≤: 0.035
Cr(%): 0.90~1.20
Mo(%): -
Ni(%): -
Other(%): V0.10~0.20
58crv4 steel structure mechanical properties - HOT WORKING, HEAT TREATMENT AND HARDNESS
|Quenching |hot working temp./℃|First: 850
|quenching|hot working temp./℃|Second: —
|quenching|cooling medium: oil
|tempering|hot working temp./℃: 600
|tempering |cooling medium: water, oil
|σb/MPa|≥: 1280
|σs/MPa|≥: 1150
|δ5(%)|≥: 10
|ψ(%)|≥: 40
|AKV/J|≥: 78
Hardness / HBS|≥: 255
58crv4 steel structure PRODUCT PROFILE
58crv4 steel structure Round bar / Wire rod (Diameter): 0.50mm to 800mm
58crv4 steel structure Square bar / Flat bar: 3mm to 1500mm
58crv4 steel structure Plate / Steel strip: 0.1mm to 1500mm
Width: 8mm to 2500mm
58crv4 steel structure Steel sheet: thickness 0.50 ~ 6.00mm, width 1000mm X length 1000/2000mm - Standard size
Length: random length or based on the customer's special requirement
as a 58crv4 steel structure exporter , any need in 58crv4 steel structure or 58crv4 steel structure chemical composition , 58crv4 steel structure MECHANICAL PROPERTIES , please contact us!
Pre: 1010 steel structure,1010 steel structure Heat treatment