SAE/AISI/ASTM 1020 I beam

Date : 2016-10-14 14:46:48

Processing

SAE/AISI/ASTM 1020 I-beam is a kind of high quality carbon structural steel with cold deformation and high plasticity. The strength of SAE /AISI/ASTM 1020 I-beam is slightly higher than No. 15 steel, very little quenching, no temper brittleness.

SAE/AISI/ASTM 1020 I beam Chemical Composition:

Material

C %

Mn  %

P  %

S %

ASTM 1020

0.18~0.23

0.30~0.60

≤0.040

≤0.050

AISI 1020

0.17~0.23

0.30~0.60

 ≤0.040

≤0.050

SAE 1020

0.18~0.23

0.30~0.60

≤0.040

≤0.050 

 
SAE/AISI/ASTM 1020 I beam Normalized Mechanical properties:

Material

Tensile Strength (M pa)

Yield Strength (M pa)

Elongation (%)

Hardness (HB)

ASTM 1020

≥410(42) M pa

≥245(25) M pa

≥25 (%)

≤156HB 

AISI 1020

394.7 M pa

294.8Mpa

36.5(%)

111HB

SAE 1020

650- 880MPa

350 - 550

8 - 25(%)

111HB

SAE/AISI/ASTM 1020 I-beam has high machinability, high strength, high ductility and good weldability. SAE/AISI/ASTM 1020 I-beam can be largely utilized in all industrial sectors in order to enhance weldability or machinability properties. It is used in a variety of applications due to its cold drawn or turned and polished finish property.

The applications of SAE/AISI/ASTM 1020 I-beam are:
It is used for simple structural application such as cold headed bolts.

Delivery Condition:
SAE/AISI/ASTM 1020 I-beam Delivery Condition
AR(As Hot Rolled), N(Normalized), T(Tempered), Q(Quenched), TMCP, Q+T(Quenched and Tempered), UT(Ultrasonic Test:ASTM A435,ASTM A578-C/B/A,EN10160-S0E1,S1E2,S2E3,S3E4), Impact Test, PWHT(Post Weld Heat Treatment), HIC, Z Test(Z15, Z25, Z35)

Contact Us

TEL : 0086-18317160019

E-mail : [email protected] 

Address : No.230,1st Floor,Building No.1,No.221 Of Huashen Road,Free Trade Area Of Pudong New District,Shanghai China