SAPH440 steel: Chemical Composition and Mechanical Properties

SAPH440 steel is structural hot-rolled steel in the form of plates, sheets & strips for automobile structural applications. SAPH440 is a material grade and designation defined inJISG 3113 standard.

The structural quality hot rolled SAPH440 steel is more reliable in its tensile strength thanSAPH400 steel. It can be used in automotive applications where more strength is needed & the material does not fail under exceeding loading.

The Chemical Composition of SAPH440 Steels

JIS G 3113 defines the chemical composition of SAPH440 steels as under:

Carbon(C) is not identified in the standard.

Manganese(Mn) is not identified in the standard.

Maximum percentage of Phosphorous(P) is0.040percent.

Maximum percentage ofSulphur(S) is0.040percent.

Remaining is iron (Fe) percentage and with few negligible impurities.

Mechanical Properties of SAPH440 Steels

The tensile strength of the SAPH440 Steels is expressed in Newton per millimeters and it must be at least 440 N/mm2 (MPa).

The yield strength is minimum 275 to minimum 305 N/mm2 (MPa) depending on the thickness.

The elongation property of SAPH440 steel varies with the ranges of thickness. The minimum percentage ranges for elongation is 29 to 34 minimum. Only over 6.5 mm thickness requires 22 minimum percentage elongations. Higher thickness gauges usually show higher elongation than lower gauges.

Dimensional Characteristics of SAPH440 Steels

The applicable thickness for this SAPH440 material as defined in the JIS 3113 starts from 2 mm to 14 mm. However, the width of SAPH440 material ranges to 950 to 2000 mm.