ASTM A537 Class 3 Plates Thickness

ASTM A537 Class 3 Plates Thickness

  ASTM A537 Class 3 plate refers to pressure vessel plates, material in heat-treated, carbon-manganese silicon steel. The maximum thickness under ASTM A537 Class 3 is 150 mm [6 inch].

  ASTM A537 Class 3 PlatesTensile Requirement

Thickness Tensile Strengthksi [MPa] Yield strengthksi [MPa], min:
2-1/2 in. and under[65 mm and under] 80-100[550-690] 55[380]
Over 2-1/2 to 4 in. [Over 65 to 100mm] 75-95[515-655] 50[345]
Over 4 to 6 in.[Over 100 to 150 mm] 70-90[485-620] 40[275]

  Elongation in 2 in[50 mm], min, %: 22

  Elongation4 in, [100 mm] and under Over 4 in [100 mm]: 20

  Heat Treatment for ASTM A537 Class 3 Plates

  A537 Class 3 plates shall be quenched and tempered. The tempering temperature for Class 2 plates shall not be less than 1100°F [595°C] and not less than 1150°F [620°C] for Class 3 plates.

  ASTM A537 Class 3 plate material is used in a variety of applications including pressurised tanks and heat exchangers. A537 Class 3 steel shall be killed and undergo normalization, quenching and tempering. A537 Class 3 Pressure Vessel Plates is mainly used for manufacture in the oil and gas and petrochemical industries. A537 cl3 steel platessupplied in the normalised condition and the specification covers plates up to 100 mm (4 inches) in thickness.

Pre: A537 cl1 Pressure Vessel Plates

Next: ASTM A285 Grade C Carbon Steel Plate

Contact Us

Shanghai Katalor Enterprises Co., Ltd

0086-18317160019
[email protected]
No.230,1st Floor,Building No.1,No.221 Of Huashen Road,Free Trade Area Of Pudong New District,Shanghai China
Live Chat